ASME SA106/SA106M

This specification covers seamless carbon steel pipe for high-temperature service (Note 1) in NPS 1/8 to NPS 48 inclusive, with nominal 9average0 wall thickness as given is ANSI B36.10. Pipe having other dimensions may be furnished provided such pipe complies with all other requirements of this specification. Pipe ordered under this specification shall be suitable for bending, flanging, and similar forming operations, and for welding. When the steel is to be welded, it is presupposed that a welding procedure suitable to the grade of steel and intended use or service will be utilized (Note 2).

NOTE 1: Consideration should be given to possible graphitization of the material at the higher temperatures at which it may be used.

NOTE 2:Grades A rather than Grades B or Grades C pipe should be used for close coiling, or cold bending.

Chemical Composition

Standard

ASTM A106, ASME SA106

Grade

A

B

C

Chemical Composition (%)

C

≤ 0.25

≤ 0.30

≤ 0.35

Si

≥ 0.10

≥ 0.10

≥ 0.10

Mn

0.27-0.93

0.29-1.06

0.29-1.06

P

≤ 0.035

≤ 0.035

≤ 0.035

S

≤ 0.035

≤ 0.035

≤ 0.035

Cr

≤ 0.40

≤ 0.40

≤ 0.40

Mo

≤ 0.15

≤ 0.15

≤ 0.15

Cu

≤ 0.40

≤ 0.40

≤ 0.40

Ni

≤ 0.40

≤ 0.40

≤ 0.40

V

≤ 0.08

≤ 0.08

≤ 0.08

Mechanical Properties

Standard

Grade

Tensile Strength (MPa)

Yield Strength (MPa)

ASTM A106 ASME SA106

A

≥ 330

≥ 205

B

≥ 415

≥ 240

C

≥ 485

≥ 275
%E7%AC%AC%E4%B8%80%EF%BC%8C%E6%9C%80%EF%BC%8C%E4%BC%98%E7%A7%80%EF%BC%8C%E5%A2%9E%E5%BC%BA%EF%BC%8C%E4%B8%80%E6%B5%81%EF%BC%8C%E5%8D%93%E8%B6%8A%EF%BC%8C%E9%A2%86%E5%85%88%EF%BC%8C%E5%85%88%E8%BF%9B%EF%BC%8C%E5%BC%95%E9%A2%86

Sorry，当前栏目暂无内容!

您可以查看其他栏目或返回 首页

Sorry，The current column has no content!

You can view other columns or return Home

Apply For Discount ！

24 Hours Online Service

Provide You With Free Industry Solutions

Quality Assurance

Submit
%{tishi_zhanwei}%